SOLID SEAL SL
High-strength, fast reacting, non-foaming 2 component injection resin based on silicate, low viscosity, high fluidity
- For grouting of water bearing cracks being > 0,2 mm
- For structural filling of cracks
- For ground and rock stabilization
- Underpinning of massive structural elements
| Mixture of A-and B-component | |
|---|---|
| Processing temperature | 15 – 30°C (substrate temperature) |
| Viscosity of mixture (23°C) | ~ 160 mPas (DIN EN ISO 2555) |
| Mixing ratio A : B | 1 : 1 (parts by vol.) |
| Reaction data at 23°C | |
| String gel time | ~ 1:20 min (ASTM D7487) |
| Final curing | ~ 20 min |
| Properties after curing: | |
| Compressive strength | ~ 51 N/mm2 (DIN EN 12190) |
| Bending tensile strength | ~ 24 N/mm2 (DIN EN 12390-5) |
| E-modulus | ~ 1100 MPa (DIN EN ISO 527) |